Cartridge Brass, UNS C26000 (260 Brass), OS070 Temper Flat ...
| Cartridge Brass, UNS C26000 (260 Brass), OS070 Temper flat products | |
|---|---|
| Categories: | Metal; Nonferrous Metal; Copper Alloy; Brass |
| Material Notes: | Fair to excellent corrosion resistance. Excellent cold workability; good hot formability. Applications: radiator cores and tanks, flashlight shells, lamp fixtures, fasteners, locks, hinges, ammunition components, plumbing accessories, pins, rivets. Test specimen: flat products - 1mm thickness. |
| Key Words: | 70/30 brass, CDA 260, CZ106, ISO CuZn30, CEN CW505L |
| Vendors: | Visit metalmen for your metals needs. Products include special chemistry, tight tolerances, custom tempers, odd dimensions/forms, and small quantities. Phone 1-800-767-9494.Click here to view all available suppliers for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.53 g/cc | 0.308 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell F | 58 | 58 | |
| Hardness, Rockwell 30T | 15 | 15 | |
| Tensile Strength, Ultimate | 315 MPa | 45700 psi | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | |
| Elongation at Break | 65 % | 65 % | In 50 mm |
| Modulus of Elasticity | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.375 | 0.375 | |
| Fatigue Strength | 90.0 MPa@# of Cycles 1.00e+8 | 13100 psi@# of Cycles 1.00e+8 | Reverse Bending |
| Machinability | 30 % | 30 % | UNS C36000 (free-cutting brass) = 100% |
| Shear Modulus | 40.0 GPa | 5800 ksi | |
| Shear Strength | 220 MPa | 31900 psi | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.9 µm/m-°C@Temperature 20.0 - 300 °C | 11.1 µin/in-°F@Temperature 68.0 - 572 °F | |
| Specific Heat Capacity | 0.375 J/g-°C | 0.0896 BTU/lb-°F | |
| Thermal Conductivity | 120 W/m-K@Temperature 20.0 °C | 833 BTU-in/hr-ft²-°F@Temperature 68.0 °F | |
| Melting Point | 915 - 955 °C | 1680 - 1750 °F | |
| Solidus | 915 °C | 1680 °F | |
| Liquidus | 955 °C | 1750 °F | |
| Processing Properties | Metric | English | Comments |
| Annealing Temperature | 425 - 750 °C | 797 - 1380 °F | |
| Hot-Working Temperature | 725 - 850 °C | 1340 - 1560 °F | |
| Component Elements Properties | Metric | English | Comments |
| Copper, Cu | 68.5 - 71.5 % | 68.5 - 71.5 % | |
| Iron, Fe |