G35C - Fondinox

Có thể bạn quan tâm

Skip to content G35C

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
G35C	–	2.4643 NiCr33Mo8	N06035	–	Hastelloy G35®

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.02	33.4	Bal.	8.3	Fe<2.0, W<0.6	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
305	565	35	180	100

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm3]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic, (Intermetallics)	8.22	12.3	10	450	1332-1361

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Solution Annealing	Satisfactory	–	1.8

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Nickel Base
ACI/CAST GRADE	G35C
CAST ASTM	–
CAST EN/DIN	2.4643 NiCr33Mo8
CAST UNS	N06035
WROUGHT UNS	–
WROUGHT GRADE	Hastelloy G35®
C	<0.02
Cr	33.4
Ni	Bal.
Mo	8.3
Other	Fe<2.0, W<0.6
PREn	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa]	305
Rm [MPa]	565
A %	35
Hardness [HB]	180
Impact [J]	100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic, (Intermetallics)
ρ [kg/dm3]	8.22
α [μm/m∙K] (20 – 100 °C)	12.3
K [W/m∙K]	10
Cp [J/kg∙K]	450
Melting ΔT [°C]	1332-1361
WORKING CONDITIONS / FABRICATION
Heat Treatment	Solution Annealing
Weldability	Satisfactory
Machining	–
Patternmaker’s Shrinkage [%]	1.8

SEARCH: Search: LAST ARTICLES

Fondinox featured in “Vite d’Impresa – 80 Years of the Associazione Industriali Cremona”19/11/2025
New molding department for large-size castings14/11/2025
Fondinox supports the first Camminata dell’Accoglienza in Sergnano28/09/2025