Both H04 C10100 copper and C11000 copper are copper alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is H04 C10100 copper and the bottom bar is C11000 copper.

Full-Hard (H04) C10100 CopperUNS C11000 (CW004A) Electrolytic Tough Pitch CopperMetric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 20
1.5 to 50
Poisson's Ratio 0.34
0.34
Rockwell F Hardness 87
37 to 94
Rockwell Superficial 30T Hardness 58
35 to 63
Shear Modulus, GPa 43
43
Shear Strength, MPa 180
150 to 230
Tensile Strength: Ultimate (UTS), MPa 320
220 to 410
Tensile Strength: Yield (Proof), MPa 280
69 to 390

Thermal Properties

Latent Heat of Fusion, J/g 210
210
Maximum Temperature: Mechanical, °C 200
200
Melting Completion (Liquidus), °C 1080
1080
Melting Onset (Solidus), °C 1080
1070
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 390
390
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
100
Electrical Conductivity: Equal Weight (Specific), % IACS 100
100

Otherwise Unclassified Properties

Base Metal Price, % relative 31
31
Density, g/cm3 9.0
9.0
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 41
41
Embodied Water, L/kg 310
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 61
6.1 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 330
21 to 640
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 9.9
6.8 to 13
Strength to Weight: Bending, points 12
9.0 to 14
Thermal Diffusivity, mm2/s 110
110
Thermal Shock Resistance, points 11
8.0 to 15

Alloy Composition

Copper (Cu), % 99.99 to 100
99.9 to 100
Lead (Pb), % 0 to 0.0010
0
Oxygen (O), % 0 to 0.00050
0
Phosphorus (P), % 0 to 0.00030
0
Zinc (Zn), % 0 to 0.00010
0
Residuals, % 0
0 to 0.1
Member Area Login Get Membership

Find Materials

Search by Property Value Browse from Home Page

Table of Contents

IntroductionMechanical PropertiesThermal PropertiesElectrical PropertiesOtherwise Unclassified PropertiesCommon CalculationsAlloy Composition

Từ khóa » C11000 Vs C10100