Abstract

A novel etch chemistry, C4H9F was evaluated for highly selective patterning of SiN using both organic and SiOx masks for line/space and cylindrical geometries. Patterning of 80 nm of SiN using 65 nm of the organic planarization layer (OPL) mask with a C4H9F:O2 admixture yielded line edge roughness (LER) and line width roughness (LWR) values of 1.9 and 2.8 nm on sub-25 nm critical dimension (CD) SiN lines at 50 nm pitch, with >50 nm mask retention up to 40% overetch values. The LER and LWR values were 60% and 66% lower than features patterned using a CF4 admixture, which also exhibited complete OPL mask loss and nitride erosion of 27 nm even at the endpointed etch condition. Using 20 nm of SiOx as a mask and removing CF4 from the chemistry admixture, LER and LWR values of 2.7 and 3.3 nm were achieved with nearly full SiOx retention for features of identical dimensions. At smaller mask pitches (21 and 24 nm) formed by directed self-assembly of high-χ block copolymers, the highly selective nature of C4H9F to organic masks facilitated SiN pattern transfer where CF4 based admixtures failed, achieving line CDs of ∼12 nm with LWR and LER of 1.6 and 2.2 nm. Applied to alternate geometry, hole patterning in SiN at ∼30 nm CD and 60 nm pitch was demonstrated. A subsequent image reversal process yielded pillars by filling the hole pattern with OPL and etching back the surrounding SiN layer, reaffirming the extremely high selectivity of C4H9F to organic masks.

Paper

In-situ etch rate study of HfxLayOz in Cl2/BCl3 plasmas using the quartz crystal microbalance

Nathan Marchack, Taeseung Kim, et al.

JVSTA

Conference paper

Defect mitigation of plasma-induced delamination of TiW/Cu from SiNx layer in thin si interposer processing with glass carriers

Vijay Sukumaran, Thuy Tran-Quinn, et al.

ECTC 2015

Conference paper

High-performance CMOS-compatible self-aligned In0.53Ga0.47As MOSFETs with GMSAT over 2200 μs/μm at VDD = 0.5 v

Yanning Sun, Amlan Majumdar, et al.

IEDM 2014

Conference paper

Electrical characterization of FinFETs with fins formed by directed self assembly at 29 nm fin pitch using a self-aligned fin customization scheme

Hsinyu Tsai, Hiroyuki Miyazoe, et al.

IEDM 2014

View all publications
  1. Home
  2. Publications

Date

01 May 2018

Publication

JVSTB

Authors

  • Nathan Marchack
  • Hiroyuki Miyazoe
  • Robert L. Bruce
  • Hsinyu Tsai
  • Masahiro Nakamura
  • Takefumi Suzuki
  • Azumi Ito
  • Hirokazu Matsumoto
  • Sebastian U. Engelmann
  • Eric A. Joseph
IBM-affiliated at time of publication

Resources

  • Publication

Share

Từ khóa » C4h9f