C95500 Bronze Vs. C95800 Bronze
Home>Copper AlloyUp Three>Cast BronzeUp Two>C95500 BronzeUp OneC95500 Bronze vs. C95800 Bronze
Member Area Login Get Membership
Both C95500 bronze and C95800 bronze are copper alloys. Their average alloy composition is basically identical. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C95500 bronze and the bottom bar is C95800 bronze.
UNS C95500 Aluminum BronzeUNS C95800 Nickel-Aluminum BronzeMetric UnitsUS Customary UnitsMechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 120 |
120 |
Elongation at Break, % | 8.4 to 10 |
22 |
Poisson's Ratio | 0.34 |
0.34 |
Shear Modulus, GPa | 44 |
44 |
Tensile Strength: Ultimate (UTS), MPa | 700 to 850 |
660 |
Tensile Strength: Yield (Proof), MPa | 320 to 470 |
270 |
Thermal Properties
Latent Heat of Fusion, J/g | 230 |
230 |
Maximum Temperature: Mechanical, °C | 230 |
230 |
Melting Completion (Liquidus), °C | 1050 |
1060 |
Melting Onset (Solidus), °C | 1040 |
1040 |
Specific Heat Capacity, J/kg-K | 450 |
440 |
Thermal Conductivity, W/m-K | 42 |
36 |
Thermal Expansion, µm/m-K | 18 |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 8.0 |
7.0 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 |
7.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 28 |
29 |
Density, g/cm3 | 8.2 |
8.3 |
Embodied Carbon, kg CO2/kg material | 3.5 |
3.4 |
Embodied Energy, MJ/kg | 57 |
55 |
Embodied Water, L/kg | 390 |
370 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 58 to 61 |
110 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 to 950 |
310 |
Stiffness to Weight: Axial, points | 8.0 |
7.9 |
Stiffness to Weight: Bending, points | 20 |
20 |
Strength to Weight: Axial, points | 24 to 29 |
22 |
Strength to Weight: Bending, points | 21 to 24 |
20 |
Thermal Diffusivity, mm2/s | 11 |
9.9 |
Thermal Shock Resistance, points | 24 to 29 |
23 |
Alloy Composition
Aluminum (Al), % | 10 to 11.5 |
8.5 to 9.5 |
Copper (Cu), % | 78 to 84 |
79 to 83.2 |
Iron (Fe), % | 3.0 to 5.0 |
3.5 to 4.5 |
Lead (Pb), % | 0 |
0 to 0.030 |
Manganese (Mn), % | 0 to 3.5 |
0.8 to 1.5 |
Nickel (Ni), % | 3.0 to 5.5 |
4.0 to 5.0 |
Silicon (Si), % | 0 |
0 to 0.1 |
Residuals, % | 0 |
0 to 0.5 |
Find Materials
Search by Property Value Browse from Home PageTable of Contents
IntroductionMechanical PropertiesThermal PropertiesElectrical PropertiesOtherwise Unclassified PropertiesCommon CalculationsAlloy CompositionTừ khóa » C95800
-
C95800 Bar & Forgings Grade - Aluminium Bronze
-
C95800 Alloy, C958 Nickel-Aluminum Bronze
-
Nickel Aluminum Bronze - Copper Casting Alloy UNS C95800 - AZoM
-
C95800 Alloy
-
C95800 Alpha Nickel Aluminum Bronze - Aviva Metals
-
ASTM C95800 - Nickel Aluminium Bronze - Copper Alloys Ltd
-
C95800 Nickel Aluminum Bronze Technical Data Sheet
-
C95800 Aluminum Bronze In Solids & Rectangles
-
Alloy Grade UNS: C95800 - Highly Flexible Alloys - MetalTek
-
ASTM B148 Grade C95800 As-Cast Or Temper-Annealed - Matmatch
-
Alpha Nickel-Aluminum Bronze, UNS C95800, Copper Casting Alloy
-
Nickel Aluminium Bronze C95800 , UNS C95800 Alloys
-
Nickel Aluminium Bronze Supplier | UNS C95800 - E Steel Sdn.Bhd
-
C95800 CDA 958 Aluminum Bronze Alloys - Conex Casting