C10200 Copper Tubing - Atlas Bronze

C10200 Copper Tubing

Atlas carries C10200 Oxygen Free (OF) Copper in Tubing. We carry a very large range of sizes and will cut the material to length.

C10200 Oxygen Free (OF) Copper is produced by the direct conversion of selected refined cathodes and castings under carefully controlled conditions to prevent contamination of the pure oxygen-free metal during processing. The method of producing OFHC copper ensures extra high grade of metal with a copper content of 99.99%. With so small a content of extraneous elements, the inherent properties of elemental copper are brought forth to a high degree.

While OF is considered oxygen-free, its conductivity rating is no better than the more common ETP or C11000 grade copper. It has a 0.001% oxygen content, 99.95% purity and minimum 100% IACS conductivity. For the purposes of purity percentage, silver (Ag) content is counted as copper (Cu).

OD (inches)	Wall (inches)	Part Number
0.500	0.125	1020T-4-1
0.625	0.125	1020T-5-1
0.750	0.032	1020T-6-0.256
0.750	0.062	1020T-6-0.496
0.875	0.032	1020T-7-0.256
0.875	0.065	1020T-7-0.52

C10200 TYPICAL USES

Some of the typical areas that C10200 is used in, is as follows: Microwave Tubes, Copper to Glass Seals in Electronic Appliances, Wave Guides, Bus Conductors, Busbars, Klystrons, Coaxial Cables, Electrical Conductors, Lead In Wire, Transistor Component, Billet Mold Tube, Coaxial Tube, Extrusion Cans for Powder Metallurgy, Vacuum Seals, Tubing, LP Gas Service, Tubing, Medical Gas- Oxygen

C10200 CHEMICAL COMPOSITION

(%max., unless shown as range or min.) NOTE: Information courtesy of copper.org

Cu (1)	O
Min./Max.	99.95 min	.0010
Nominal	-	-

(1) Cu value includes Ag. Note: This is a high conductivity copper which has, in the annealed condition a minimum conductivity of 100% IACS except for Alloy C10100 which has a minimum conductivity of 101% IACS.

C10200 MECHANICAL PROPERTIES

(measured at room temperature, 68 F (20 C) NOTE: Information courtesy copper.org

Temper	SectionSize	ColdWork	Typ/Min	Temp	TensileStrength	YieldStrength(0.5% ext.under load)	YieldStrength(0.2%offset)	YieldStrength(0.05%offset)	El	RockwellHardness				VickensHard.	BrinellHard.		ShearStrength	FatigueStrength*	IzodImpactStrength
in.	%	F	ksi	ksi	ksi	ksi	%	B	C	F	30T	500	500	3000	ksi	ksi	ft-lb
mm.	C	MPa	MPa	MPa	MPa	MPa	MPa	J
Flat Products
H02	0.04	0	TYP	68	42	36	-	-	14	40	-	84	50	-	-	-	26	13	0.0
1	20	290	248	-	-	14	40	-	84	50	-	-	-	179	90	0.0
M20	0.25	0	TYP	68	32	10	-	-	50	-	-	40	-	-	-	-	22	-	0.0
6.35	20	221	69	-	-	50	-	-	40	-	-	-	-	152	-	0.0
H04	0.25	0	TYP	68	50	45	-	-	12	50	-	90	-	-	-	-	28	-	0.0
6.35	20	345	310	-	-	12	50	-	90	-	-	-	-	193	-	0.0
Rod
M20	1	0	TYP	68	32	10	-	-	55	-	-	40	-	-	-	-	22	-	0.0
25.4	20	221	69	-	-	55	-	-	40	-	-	-	-	152	-	0.0
Shapes
M30	0.5	0	TYP	68	32	10	-	-	50	-	-	40	-	-	-	-	22	-	0.0
12.7	20	221	69	-	-	50	-	-	40	-	-	-	-	152	-	0.0
M20	0.5	0	TYP	68	32	10	-	-	50	-	-	40	-	-	-	-	22	-	0.0
12.7	20	221	69	-	-	50	-	-	40	-	-	-	-	152	-	0.0
Flat Products
H04	0.04	0	TYP	68	50	45	-	-	6	50	-	90	57	-	-	-	28	13	0.0
1	20	345	310	-	-	6	50	-	90	57	-	-	-	193	90	0.0
Rod
H04	0.25	40